Fracture behavior of bimetallic Al-Cu LBW joints

dc.creatorHaidemenopoulos, G. N.en
dc.creatorZervaki, A. D.en
dc.creatorKamoutsi, H.en
dc.creatorHontzopoulos, E.en
dc.creatorMangana, F.en
dc.date.accessioned2015-11-23T10:29:31Z
dc.date.available2015-11-23T10:29:31Z
dc.date.issued2013
dc.identifier.isbn9789608810433
dc.identifier.urihttp://hdl.handle.net/11615/28320
dc.description.abstractPulsed laser spot welding of copper tubing to aluminum sheet is currently used for the construction of solar thermal absorbers. The bimetallic joints should withstand high thermal stresses during the operation of the absorber. Among others, major influence on the fracture behavior of these joints comes from the intermetallic compounds, which form during the solidification of the weld metal. In this study several bimetallic Al-Cu spot welds have been produced by employing a Nd:YAG laser with a variable pulse shape. The welds have been characterized metallographically. Simple pull-up tests have been employed in order to assess the static strength of the joints. The fracture surfaces have been investigated with SEM. A correlation between intermetallic compound formation and fracture behavior is established.en
dc.source.urihttp://www.scopus.com/inward/record.url?eid=2-s2.0-84905699248&partnerID=40&md5=6ee358a40b360d19fff83ccdc6c2248c
dc.subjectBimetallic jointsen
dc.subjectIntermetallic compoundsen
dc.subjectPulsed laser spot weldingen
dc.subjectFracture mechanicsen
dc.subjectIntermetallicsen
dc.subjectNeodymium lasersen
dc.subjectPulsed lasersen
dc.subjectSafety engineeringen
dc.subjectSoldering alloysen
dc.subjectSpot weldingen
dc.subjectCopper tubingen
dc.subjectFracture behavioren
dc.subjectFracture surfacesen
dc.subjectLaser spot weldingen
dc.subjectND : YAG lasersen
dc.subjectSolar thermal absorbersen
dc.subjectStatic strengthen
dc.subjectAluminumen
dc.titleFracture behavior of bimetallic Al-Cu LBW jointsen
dc.typeconferenceItemen